grade : KA-101
Applications: Used for reclaiming degradation product in the work solution of hydrogen peroxide producing by Anthraquinone Prosess.
|
Name of goods |
Alumina for hydrogen peroxide producing |
|
Mark |
KA-101 |
|
Crystalline Phase |
γ-Al2O3 |
|
Appearance |
WHITE SPHERE |
|
Sphere Size(mm) |
7-14MUSH Φ3-5 Φ4-6 Φ5-7 |
|
Bulk Density(g/cm3) |
0.68-0.75 |
|
Crush resistance(N/sphere) |
50 Min |
|
Specific Surface(m2/g) |
200-260 |
|
Pore Volume(cm3/g) |
0.40-0.46 |
|
Macropores（≥750?） |
0.14 |
|
Water absorption（wt%） |
50 Min |
grade : KA-102
Applications: Activated Alumina drier is used for deep drying of gas or liquid phase in petrochemicals production and absorption drying by automatic instruments.
|
Name of goods
|
Activated Alumina Drier
|
|
Mark |
KA-102 |
|
Crystalline Phase |
x-ρ Al2O3 |
|
Appearance |
WHITE SPHERE |
|
Sphere Size(mm) |
Φ3-5 Φ4-6 Φ5-7 Φ8-10 |
|
Bulk Density(g/cm3) |
0.68-0.89 |
|
Crush resistance(N/sphere) |
130Min |
|
Specific Surface(m2/g) |
280-360 |
|
Pore Volume(cm3/g) |
0.38-0.40 |
|
18Min |
grade : KA-103
Applications: Activated Alumina for defluorination
|
Name of goods No. HS |
Activated Alumina for defluorination |
|
Mark |
KA-103 |
|
Appearance |
WHITE SPHERE |
|
Sphere Size (mm) |
Φ1.5-2 Φ2-3 Φ4-6 Φ5-7 |
|
Bulk Density (g/cm3) |
0.75Min |
|
Crush resistance (N/sphere) |
50-80 |
|
Specific Surface (m2/g) |
280-360 |
|
0.40 |
|
|
Defluorination (mgF/g Al2O3) |
1.2Min |
grade : KA-104
Applications: special deliming agent for PE
|
Name of goods No. HS |
Alumina deliminger for PE
|
|
Mark |
KA-104 |
|
Appearance |
WHITE SPHERE |
|
Sphere Size |
7-14MESH |
|
Bulk Density(g/cm3) |
0.78-0.86 |
|
Crush resistance(N/sphere) |
48Min |
|
Abrasion Loss（wt%） |
0.5Max |
|
Specific Surface(m2/g) |
280Min |
|
Pore Volume(cm3/g) |
0.43 |
grade : KA-105
Applications: special drier used drying of Chloropropylene and PTA
|
Name of goods No. HS |
Alumina gel drier
|
|
Mark |
KA-105 |
|
Appearance |
WHITE SPHERE |
|
Sphere Size(mm) |
Φ3-5 Φ4-6 |
|
Bulk Density(g/cm3) |
0.76-0.82 |
|
Crush resistance(N/sphere) |
130Min |
|
Abrasion Loss（wt%） |
0.3Max |
|
Specific Surface(m2/g) |
330Min |
|
Pore Volume(cm3/g) |
0.40-0.45 |
|
Macropores（>750?） |
0.14 |
grade : KC-201
Applications:
|
Name of goods No. HS |
Alumina for sulfur recovery in Claus Prosess |
|
Mark |
KC-201 |
|
Appearance |
WHITE SPHERE |
|
Sphere Size(mm) |
Φ4-6 |
|
Bulk Density(g/cm3) |
0.68-0.72 |
|
Crush resistance(N/sphere) |
130Min |
|
Specific Surface(m2/g) |
300Min |
|
Pore Volume(cm3/g) |
0.40 |
grade : KC-202
Applications: deoxidation Catalyst for sulfur recovery
|
Name of goods No. HS |
deoxidation Catalyst for sulfur recovery |
|
Mark |
KC-202 |
|
Appearance |
REDDISH BROWN SPHERE |
|
Sphere Size(mm) |
Φ4-6 |
|
Bulk Density(g/cm3) |
0.70-0.75 |
|
Crush resistance(N/sphere) |
130Min |
|
Specific Surface(m2/g) |
260Min |
grade : KC-203
Applications: Tail gas hydrogenation catalyst and catalyst carrier
|
Name of goods No. HS |
Tail gas hydrogenation catalyst and catalyst carrier
|
|
|
Mark |
KC-203 |
|
|
Appearance |
SPHERE |
|
|
Sphere Size(mm) |
Φ4-5 |
|
|
Bulk Density(g/cm3) |
0.68Min |
|
|
Crush resistance(N/sphere) |
130 |
|
|
Specific Surface(m2/g) |
180Max |
|
|
Pore Volume(cm3/g) |
0.50Min |
|
|
Na2O% |
0.05Max |
|
|
Active constituent% |
C0O |
4.0Min |
|
M0O3 |
12 |
|
grade : KACC-301
Applications:
|
Name of goods No. HS |
Pd-catalyst carrier |
||
|
Mark |
KACC-301 |
||
|
Crystalline Phase |
r-Al2O3 |
||
|
Appearance |
WHITE SPHERE |
||
|
Φ1.5-2 |
Φ2-3 |
Φ3-4 |
|
|
Bulk Density(g/cm3) |
0.2-0.3 |
0.4-0.5 |
0.6-0.7 |
|
Specific Surface(m2/g) |
160Min |
200Min |
300Min |
|
Crush resistance(N/sphere) |
10 Min |
30 Min |
60 Min |
|
Pore Volume(cm3/g) |
0.5 |
||
grade : KACC-302
Applications: TiO2-Al2O3 catalyst carrier and catalyst
|
Name of goods No. HS |
TiO2-Al2O3 catalyst carrier and catalyst |
|
|
Mark |
KACC-302 |
|
|
Al2O3 |
80Min |
|
|
TiO2 |
6Min |
|
|
Appearance |
WHITE SPHERE |
|
|
Sphere Size(mm) |
Φ2-3 Φ3-5 Φ4-6 |
|
|
Bulk Density(g/cm3) |
0.68-0.75 |
|
|
Crush resistance(N/sphere) |
60-180 |
|
|
Specific Surface(m2/g) |
200Min |
300Min |
|
Pore Volume(cm3/g) |
0.38 |
0.55 |
grade : KACC-303
Applications: Catalyst carrier for COS hydrolysis
|
Name of goods No. HS |
Catalyst carrier for COS hydrolysis |
|
Mark |
KACC-301 |
|
Crystalline Phase |
r-Al2O3 |
|
Appearance |
WHITE SPHERE |
|
Sphere Size(mm) |
Φ3-5 Φ4-6 |
|
Bulk Density(g/cm3) |
0.68-0.72 |
|
Crush resistance(N/sphere) |
60Min |
|
Specific Surface(m2/g) |
200Min |
|
Pore Volume(cm3/g) |
0.45 |
grade : KACC-304
Applications: Catalyst carrier for sulfate resisting conversion
|
Name of goods No. HS |
Catalyst carrier for sulfate resisting conversion |
|
Mark |
KACC-304 |
|
Crystalline Phase |
r-Al2O3 |
|
Appearance |
WHITE SPHERE |
|
Sphere Size(mm) |
Φ2-3 Φ3-5 Φ4-6 |
|
Bulk Density(g/cm3) |
0.53-0.65 |
|
Crush resistance(N/sphere) |
60-180 |
|
Specific Surface(m2/g) |
200Min |
|
Pore Volume(cm3/g) |
0.45Min |
|
Water absorption（wt%） |
60Min |
grade : KACC-305
Applications:
|
Name of goods No. HS |
Dseudo boehmite Alumina powder |
|
Mark |
KACC-305 |
|
Crystalline Phase |
Pseudoboehmite |
|
Specific Surface(m2/g) |
280Min |
|
Pore Volume(cm3/g) |
0.45-0.50 |
|
Al2O3% |
72Min |
|
SiO2% |
0.03Max |
|
Fe2O3 |
0.03Max |
|
Na2O% |
0.1Max/0.05Max |
|
Sphere Size（mush） |
300 |
grade : KACC-306
Applications:
|
Name of goods No. HS |
Macropore pseudo boehmite |
||
|
Mark |
KACC-306 |
||
|
Crystalline Phase |
pseudoboehmite |
||
|
Bulk Density(g/cm3) |
0.20Max |
HYC-207-2 0.08Max |
|
|
Specific Surface(m2/g) |
200Min |
||
|
Pore Volume(cm3/g) |
0.8 |
2.0 |
|
|
Na2O% |
0.02Max |
0.02 Max |
|
|
Sphere Size （μm） |
3-4 |
1Max |
|
grade : KACC-307
Applications: Roll Alumia Carrier
|
Name of goods No. HS |
Roll Alumia Carrier |
|
Mark |
KACC-307 |
|
Crystalline Phase |
α-Al2O3 |
|
Appearance |
Rollor Φ3×10-15 Φ2×10-15 Φ5×10-15 |
|
Specific Surface(m2/g) |
200-300 |
|
Pore Volume(cm3/g) |
0.40-0.46 |
|
Na2O% |
0.05Max |
grade : KM-401
Applications:
|
No. HS |
MOLECULAR SIEVE 3A |
|
Mark |
KM-401 |
|
Sphere Size(mm) |
Φ1.6×10-12 Φ3×10-12 |
|
Appearance |
BROWN SPHERE OR BAR |
|
Bulk Density(g/cm3) |
0.68-0.72 |
|
Crush resistance(N/sphere) |
10-80 |
|
Abrasion Loss（wt%） |
0.30 |
|
Static Absorption capacity （RH60%） |
21±2 |
grade : KM-402
Applications:
|
Name of goods No. HS |
MOLECULAR SIEVE 4A |
|
Mark |
KM-402 |
|
Sphere Size(mm) |
Φ2-3 Φ3-4 Φ4-6 |
|
Appearance |
BROWN SPHERE |
|
Bulk Density(g/cm3) |
0.68-0.72 |
|
30-80 |
|
|
Abrasion Loss（wt%） |
0.30 |
|
Static Absorption capacity （RH60%） |
21±2 |
grade : KM-403
Applications:
|
Name of goods No. HS |
MOLECULAR SIEVE 5A |
|
Mark |
KM-403 |
|
Sphere Size(mm) |
Φ2-3 Φ3-5 Φ4-6 |
|
Appearance |
BROWN SPHERE |
|
Bulk Density(g/cm3) |
0.68-0.72 |
|
Abrasion Loss（wt%） |
0.30 |
|
Static Absorption capacity （RH60%） |
21±2 |
grade : KM-404
Applications:
|
Name of goods No. HS |
MOLECULAR SIEVE 13X |
|
Mark |
KM-404 |
|
Sphere Size(mm) |
Φ2-3 Φ3-5 Φ4-6 |
|
Appearance |
BROWN SPHERE |
|
Bulk Density(g/cm3) |
0.68-0.72 |
|
Crush resistance(N/sphere) |
30-80 |
|
Abrasion Loss（wt%） |
0.30 |
|
Static Absorption capacity （RH60%） |
24 |